Nozzle Filling Compound is the high refractory material which is a result of a very successful amalgamation of all good products, thus have excellent flow. Ladle Nozzle filling compound is chromite, Zirconia, Alumina, and Silica-based that is custom made as per prevailing plant Practices. Ladle Nozzle Filling Compound is designed on the most successful combination of ingredients in controlled sizes in appropriate ratios as revealed by experiments in simulation conditions. Ladle Nozzle filling compound gives free openings consistently, reduces ladle turnaround time, offer more production of better quality due to greatly reduced lancing and effective coating technique makes it less polluting.

Other Details:

Specification NFC-S NFC-C NFC-Z
Al2O3 10.00% 6.60% 6.60%
FeO 5.00% 8.20% 2.00%
SiO2 85.00% 54.30% 30.00%
C 2.00% 2.00% <2>
Moisture <1> <1> <1>
Cr2O3 - 22.50% 25.00%
ZrO2 - - 25.00%
MgO - 4.30% 2.00%


Benefits:
As it posses selected granulometry and high refractoriness. It does not sinter when in contact with molten steel around 1600 deg. C temperature with ferrostatic when kept in ladle well cavity. Thus it results into free flowing of NFC when slide gate is opened and it comes out freely or with minor oxygen lancing establishing a very smooth stream from the ladle Minimum Oxygen lancing or poking Acts as the desulphurizing agent also prevents the ladle from not getting utilized in casting.